Liquid crystal cell and method of manufacture

ABSTRACT

A LC cell is manufactured by the method including the steps of: rubbing a first alignment layer coating a first substrate, such that the first alignment layer has a first pretilt angle associated therewith; exposing said second alignment layer coating a first substrste to light such that said second alignment layer has at least one second pretilt angle associated therewith; and providing a liquid crystal material between said first and second substrates. The materials for the first and second alignment layers include a polyimide and a polysiloxane based material.

BACKGROUND OF THE INVENTION

[0001] The present invention is related to a liquid crystal cell, more particularly to a liquid crystal cell which is including one substrate coated with rubbed alignment layer and the other substrate coated with photo-aligned alignment layer, and the method for fabricating that.

[0002] Generally, the liquid crystal cell is comprising of two substrates and liquid crystal formed between these substrates, the liquid crystal comprising anisotropic molecules. To provide an orderly alignment of liquid crystal in the cell for the uniform brightness and the high contrast ratio of the liquid crystal cell, convnetionally rubbing is carried out on alignment layers coating substrate. The rubbing is mechanical firiction on the alignment layer so as to provide a pretilt of liquid crystal molecules defined by a pretilt angle and a pretilt angle direction. The pretilt angle refers a polar angle and the pretilt angle direction refers a azimuthal angle between the surface of alignment layer and the pretilt.

[0003] The pretilt of a liquid crystal molecule adjacent a first alignment layer is called a first pretilt of a first alignment layer, and the pretilt of a liquid crystal molecule adjacent a second alignment layer is called a second pretilt of a second alignment layer. Thereby, the pretilt of a liquid crystal molecule in the midle of two layers is determed by the interaction between pretilts of the first and second alignment layer.

[0004] The liquid crystal cell is classified a vertical aligned liquid crystal cell and a horizontal aligned liquid crystal cell depending the pretilt angle. The vertical aligned liquid crystal cell typically defines a liquid crystal cell having a pretilt angle of an alignment layer larger than 600, the horizontal algined liquid crystal cell typically refers a liquid crystal cell having a pretilt angle of an alignment layer less than 5°.

[0005] There are several modes liquid crystal cell according to relationships between a first pretilt angle direction of a first alignment layer and a second pretilt angle direction of a second alignment layer facing the first substrate. If the first pretilt angle direction is perpendicular to the second alignment direction, it is called a twisted nematic (TN) mode liquid crystal cell. If they are parallel with each other, the liquid crystal cell is called an electrically controlled birefringence (ECB) mode liquid crystal cell and a bend mode liquid crystal cell. In addition, it is called a In-Plane Switching (IPS) mode liquid crystal cell if a pretilt angle direction is shift depending on the voltafe.

[0006] A conventionally used liquid crystal display is mainly a twisted nematic liquid crystal display (TNLCD), in which the transmittance is dependent according to the viewing angle at each gray level. Especially, while the transmittance is symmetrical in the horizontal direction, the transmittance is asymmetrical in the vertical direction. Therefore, in the vertical direction, the range with inverted image phenomenon is occurred so that the vertical viewing angle becomes very limited.

[0007] To overcome said problems, a multi-domain TNLC cell such as a two-domain liquid crystal cell, and a four-domain liquid crystal cell is introduced. The multi-domain liquid crystal cell has a wider viewing angle by providing more than domains in each pixel, domains having different pretilts each other, so as to compensate the viewing angle dependence of each domain.

[0008] The most popular process to obtain said multi-domain liquid crystal cell is mechanical rubbing process, as shown in FIG. 1. Rubbing is performed mechanically on entire substrate 1 coated with alignment layer 8 such as polyimide, so that microgrooves are formed on the surface of the alignment layer 8, as shown in FIG. 1a, and FIG. 1b. To divide two domains in a pixel, in FIG. 1c and FIG. 1d, a photoresist 11 is coated entire alignment layer 8 surface, and the photoresist 11 of one domain is removed by exposing light, reverse rubbing process is carried out on one domain as shown in FIG. 1e. The remained photoresist is removed by exposing light, then, two domains are provided on the substrate 1 as shown in FIG. 1f. In the two-domain liquid crystal cell obtained thereby, the inversion of viewing angle is compensated by aforementioned process.

[0009] However, the rubbing process causes a dust particle and/or an electrostatic discharge, so the yield is reduced and/or the substrate is damaged. The manufacturing process becomes too complicated to apply industry, because the process includes a photolithography which is coating photoresist layer and removing a part of the layer by exposing light, for dividing domains.

[0010] Therefore, it is a photo-alignment method that is introduced to simplify alignment process as well as to prevent the damage of substrate. The photo-alignment is the process in which a pretilt angle direction of alignment layer is given by the irradiation of linearly polarized ultraviolet light. The alignment layer used in the photo-alignment method is mainly including PVCN (polyvinyl cinnamate). When ultraviolet light is irradiated into the photo-aligned layer coating the substrate, it causes cyclo-addition between the cinnamoyl groups of cinnamic acid side chains that belong to different photopolymers. Thereby, the direction of the photopolymer configuration i.e., the pretilt of alignment layer is aligned uniformly.

[0011] One example of the photo-alignment method is disclosured as a following process. The photo-alignment method is comprising double exposure of linearly polarized ultraviolet light into a substrate coated with PVCN to determine a pretilt, the pretilt including an alignment direction, a pretilt angle direction and pretilt angle. First linearly polarized ultraviolet light is perpendicularly irradiated into the alignment layer coating substrate so as to determine a plurality of pretilt angle direction. Then, second linearly polarized light is obliquely irradiated into the alignment layer again, to determine a pretilt angle and a pretilt angle direction. The pretilt angle and pretilt angle direction are obtained by controlling the second oblique direction relative to the substrate coated with the alignment layer.

[0012] However, the photo-alignment method has problems that the process is complicated due to the double exposure and the pretilt angle is too small, for example, the obtained pretilt angles being approximately 0.15°, 0.26° and 0.30° respectively when the oblique irradiation angles are 30°, 45° and 60°. In addition, it takes long time to irradiate light into the alignment layer so total tact time is prolonged, as well, the alignment stability of photo-alignment method is weaker than that of rubbing method.

SUMMARY OF THE INVENTION

[0013] An object of the present invention is to provide a liquid crystal cell having an alignment stability and a wilder viewing angle by simply process and the fabrication method thereof.

[0014] To achieve the object mentioned above, the method for fabricating the liquid crystal cell of the present invention is comprising the following steps of: providing a first alignment layer on a first substrate; rubbing said first alignment layer such that said first alignment layer has a first pretilt angle associated therewith; providing a second alignment layer on a second substrate; exposing said second alignment layer to light such that said second alignment layer has at least one second pretilt angle associated therewith; and providing a liquid crystal material between said first and second substrates.

[0015] The first alignment layer is comprising polyimide, but the second alignment layer is comprising photopolymers, the photo-polymers including polysiloxane based materials. The pretilt angle of this invention is controlled depending upon the photo-energy of the ultraviolet light irradiating.

[0016] To determined the second pretilt, this invention includes double irradiation of this invention. The double irradiation is comprising steps of: irradiating polarized light in the perpendicular direction to the second alignment layer and irradiating unpolarized light in the oblique direction to the second alignment layer. In this steps, the latter step can be prior to the former.

[0017] Another method for determining the second pretilt in this invention is using flowing effect. The method is comprising the steps of: irradiating polarized light in the perpendicular direction to the second substrate so as to determine a second pretilt angle and two pretilt angle direction; and injecting liquid crystal materials between said first substrate and said second substrate in the perpendicular direction to the polarized direction of the light so as to select a pretilt angle and a second pretilt angle direction.

[0018] These and other objects and advantages of the present invention will become clear from the following description of preferred embodiments.

BRIEF DESCRIPTION OF THE DRAWINGS

[0019]FIG. 1 is showing a conventional reverse-rubbing process.

[0020]FIG. 2 is showing a cross-sectional view of liquid crystal cell according to this invention.

[0021]FIG. 3 is showing a photo-irradiation device used for photo-alignment process.

[0022]FIG. 4 is a graph illustrating the relationship between the photo-energy of ultraviolet light and the pretilt angle of the photo-aligned layer formed with polysiloxane based materials.

[0023]FIG. 5 is one process for fabricating a liquid crystal cell according to this invention.

[0024]FIG. 6 is another process for fabricating a liquid crystal cell according to this invention.

[0025]FIG. 7 is a showing a cross-sectional view of a TN mode liquid crystal cell according to this invention

[0026]FIG. 8 is a showing a cross-sectional view of a ECB mode liquid crystal cell according to this invention.

[0027]FIG. 9 is a showing a cross-sectional view of a bend mode liquid crystal cell according to this invention.

[0028]FIG. 10 is a showing a cross-sectional view of a IPS mode liquid crystal cell according to this invention.

[0029]FIG. 11 is a showing one process for fabricating a multi-domain liquid crystal cell according to this invention.

[0030]FIG. 12 is another process for fabricating a multi-domain liquid crystal cell according to this invention.

[0031]FIG. 13 is another process for fabricating a multi-domain liquid crystal cell according to this invention.

[0032]FIG. 14 is another process for fabricating a multi-domain liquid crystal cell according to this invention.

DETAILED DESCRIPTION OF INVENTION

[0033]FIG. 2 is a drawing showing the liquid crystal cell, and 1 and 2 indicate a first substrate and a second substrate of the liquid crystal cell, respectively. The first substrate 1 is coated with the first alignment layer 8 formed with polyimide and is rubbed so as to determine a first pretilt defined a first pretilt angle and a first pretilt angle direction. The second substrate 2 is coated with the second alignment layer 9. The material for the second alignment layer 9 includes photo-polymers such as polysiloxane based materials. Polysiloxane cinnamate, one of the polysiloxane based materials have following structural formulas:

[0034] Polysiloxane Cinnamate I:

[0035] Z can be selected from the group consisting of OH, CH₃ or from mixtures thereof,

[0036] m=10−100,

[0037] l=1−11,

[0038] L=0 or 1,

[0039] K=0 or 1,

[0040] X, X₁, X₂, Y=H, F, Cl, CN, CF₃, C_(n)H_(2n+1) or OC_(n)H_(2n+1) wherein n can be from 1 to 10, or from mixtures thereof;

[0041] Polysiloxane Cinnamate II:

[0042] Z can be selected from the group consisting of OH, CH₃ or from mixtures thereof,

[0043] m=10−100,

[0044] l=1−11,

[0045] L=0 or 1,

[0046] K=0 or 1,

[0047] X, X₁, X₂, Y=H, F, Cl, CN, CF₃, C_(n)H_(2n+1) or OC_(n)H_(2n+1) wherein n can be from 1 to 10, or from mixtures thereof.

[0048] Then, the second substrate 2 coated with a second alignment layer 9 is exposed ultraviolet light by a photo-irradiation device in FIG. 3. The device includes the lamp 3 generating ultraviolet light, a lens 4 and a polarizer 5 linearly polarizing the ultraviolet light from lamp 3. To irradiate ultraviolet light into the alignment layer 9 of the substrate 2, the ultraviolet light generated from the lamp 3 is passed the lens 4 and linearly polarized through polarizer 5, then the ultraviolet light is irradiated into the alignment layer 9 coating substrate 2. The lamp 3 is the Mercury(Hg) lamp having the wave length of 365 nm.

[0049] In that time, the pretilt angle formed on the alignment layer 9 can be controlled by photo-energy. When ultraviolet light is perpendicularly irradiated into the substrate 2 coated with alignment layer 9 of polysiloxane based materials, the pretilt angle of the alignment layer 9 surface is controlled in a broad range according to the photo-energy of the ultraviolet light, as shown in FIG. 4. Referring to this figure, the pretilt angle can be controlled depending the photo-energy irradiated into the alignment layer 9 (the wavelength of ultraviolet light is 350 nm). The pretilt angle is exponentially get down according to the photo-energy of ultraviolet light to at almost 0° at 6,000 mJ/cm.

[0050] The vertical aliged liquid crystal cell can be fabricated by adopting photo-energy less than 2,000 mJ/cm², and the horizontal aligned liquid crystal cell can be fabricated by adopting photo-energy more than 5,000 mJ/cm².

[0051]FIG. 5 is showing one embodiment of a process for fabricating a liquid crystal cell which comprises a first substrate, a second substrate and a liquid crystal layer injected therebetween. The first substrate 1 coated with a first alignment layer 8 is mechanically rubbed to determine a pretilt, the pretilt meaning a pretilt angle and a pretilt angle direction, as shown in FIG. 5a and FIG. 5b.

[0052] The polarized light is irradiated in the perpendicular direction onto the second substrate 2 coated with a second alignment layer 9 so as to determine a second pretilt angle and two pretilt angle direction facing each other as shown in FIG. 5c and FIG. 5d. To select one pretilt angle direction, nonpolarized light is irradiated in the oblique direction onto the alignment layer 9 on the substrate 2 so as to determine a second pretilt oriented with one pretilt angle direction. In FIG. 5f, attaching the first substrate 1 and the second substrate 2, liquid crystal materials are injected between two substrates 1,2 so as to align uniformly by the stable anchoring provided by the first pretilt.

[0053] In addition, it is also possible that the oblique-irradiation can be carried out prior to the perpendicular irradiation in this embodiment.

[0054]FIG. 6 is showing another embodiment of a process for fabricating a liquid crystal cell which comprises a first substrate, a second substrate and a liquid crystal layer injected therebetween. The first substrate 1 is coated with a first alignment layer 8 is mechanically rubbed to determine a pretilt, the pretilt meaning a pretilt angle and a pretilt angle direction, as shown in FIG. 6a and FIG. 6b.

[0055] The polarized light is irradiated in the perpendicular direction into the second substrate 2 coated with a second alignment layer 9 so as to determine a second pretilt angle and two pretilt angle direction facing each other as shown in FIG. 6c and FIG. 6d. To select one pretilt angle direction, this embodiment adopts the flowing effect of liquid crystal materials in which the pretilt angle direction is determined according to the flowing direction of liquid crystal material flown as shown in FIG. 6e, FIG. 6f. Attaching the first substrate 1 having uni-pretilt determined alignment layer 8 by rubbing and second substrate 2 having two pretilts oriented with two pretilt angle directions determined a photo-aligned layer 9, then liquid crystal materials are injected between two substrates. By the flowing effect of liquid crystal materials, the liquid crystal materials adjacent the second alignment layer 9 is aligned uni-second pretilt angle direction by a single exposure.

[0056] There are several mode of liquid crystal cell depending the configuration between the first pretilt angle direction and the second pretilt angle direction determined by either abovementioned process.

[0057]FIG. 7 is reffering a TN mode liquid crystal cell. FIG. 7a and FIG. 7b are showing a vertical aligned liquid crystal cell controlling depending upon the voltage. FIG. 7c and FIG. 7d are showing a horizontal aligned liquid crystal cell.

[0058]FIG. 8 is reffering a ECB mode liquid crystal cell. FIG. 8a and FIG. 8b are showing a vertical aligned liquid crystal cell controlling depending upon the voltage. FIG. 8c and FIG. 8d are showing a horizontal aligned liquid crystal cell.

[0059]FIG. 9 is reffering a bend mode liquid crystal cell. FIG. 9a and FIG. 9b are showing a vertical aligned liquid crystal cell controlling depending upon the voltage. FIG. 9c and FIG. 9d are showing a horizontal aligned liquid crystal cell.

[0060]FIG. 10 is reffering a IPS mode liquid crystal cell in which the liquid crystal molecules are shift in plane dependind on the voltage.

[0061] This invention can be applied in a multi-domain liquid crystal cell to provide wider viewing angle. Some embodiments of process for manufacturing the multi-domain liquid crystal cell are in FIG. 11, FIG. 12, FIG. 13 and FIG. 14.

[0062]FIG. 11 is showing one embodiment of this invention to provide a multi-domain liquid crystal cell in which the first alignment layer 8 is provided a first pretilt by mechanically rubbing, and the second alignment layer 9 is provided two pretilts in two domains by using the light.

[0063]FIG. 11a and FIG. 11b is showing the rubbing process to provide a first pretilt on the alignment layer 8 with low pretilt angle, almost 0°. FIG. 11c-FIG. 11f are showing the process for forming two second pretilts on two domains of the second alignment layer 9 with a high photo-energy to provide low pretilt angle less than 5°. The polarized light is irradiated in the perpendicular direction onto the second alignment layer 9 so as to determined a second pretilt angle and two pretilt angle direction, as shown in FIG. 11d. To select a first pretilt angle direction for a first domain I, the nonpolarized light is irradiated in the first oblique direction to the second substrate 2 in which a second domain II is covered with the mask 10. Thereby, the 2-1th pretilt is formed on a first domain I, the 2-1th pretilt defined a second pretilt angle and a first pretilt angle direction, as shown in FIG. 11e.

[0064] To select a 2-2th pretilt angle direction for a second domain II, the mask 10 covering the second domain II is moved to the first domain I. The nonpolarized light is irradiated in the second oblique direction to the second substrate 2 in which a first domain I is covered with the mask 10. Thereby, the 2-2th pretilt is formed on a second domain II, as shown in FIG. 11f, the 2-2th pretilt meaning a second pretilt angle and a second pretilt angle direction.

[0065] Assembling the first substrate 1 and the second substrate 2, liquid crystal materials are injected between two substrates 1,2. The molecules of liquid crystal materials are arranged in the different direction between domains as shown in FIG. 11g depending the second pretilts.

[0066] Thereby, the viewing angle is compensated by differently aligning the liquid crystal molecules according to domains so as to get a wider viewing angle liquid crystal cell.

[0067] In this embodiment, the two-domain liquid crystal cell is possible to obtain multi-domain liquid crystal cell without photolithograpy. In addition, the alignment stability is provided by the first pretilt.

[0068]FIG. 12 is showing another embodiment of this invention to provide a vertical aligned mode multi-domain liquid crystal cell in which the first alignment layer 8 is provided a first pretilt by mechanically rubbing, and the second alignment layer 9 is provided two pretilts in two domains by using the light.

[0069]FIG. 12a and FIG. 12b is showing the rubbing process to provide a first pretilt on the alignment layer 8 with high pretilt angle larger than 60°. FIG. 12c-FIG. 12f are showing the process for forming two second pretilts on two domains of the second alignment layer 9 with a low photo-energy to provide high pretilt angle less than 60°. The polarized light is irradiated in the perpendicular direction onto the second alignment layer 9 so as to determined a second pretilt angle and two pretilt angle direction, as shown in FIG. 12d. To select a first pretilt angle direction for a first domain I, the nonpolarized light is irradiated in the first oblique direction to the second substrate 2 in which a second domain II is covered with the mask 10. Thereby, the 2-1th pretilt is formed on a first domain I, the 2-1th pretilt defined a second pretilt angle and a first pretilt angle direction, as shown in FIG. 12e.

[0070] To select a 2-2th pretilt angle direction for a second domain II, the mask 10 covering the second domain II is moved to the first domain I. The nonpolarized light is irradiated in the second oblique direction to the second substrate 2 in which a first domain I is covered with the mask 10. Thereby, the 2-2th pretilt is formed on a second domain II, as shown in FIG. 12f, the 2-2th pretilt meaning a second pretilt angle and a second pretilt angle direction.

[0071] Assembling the first substrate 1 and the second substrate 2, liquid crystal materials are injected between two substrates 1,2. The molecules of liquid crystal materials are arranged in the different direction between domains as shown in FIG. 12g depending the second pretilts. This vertical algined liquid crystal cell has a bend mode in the first domain I and a ECB mode in the second domain II.

[0072] Thereby, the viewing angle is compensated by differently aligning the liquid crystal molecules according to domains so as to get a wider viewing angle liquid crystal cell.

[0073] In this embodiment, the two-domain liquid crystal cell is accomplished by low photo-energy so it is possible to obtain multi-domain liquid crystal cell without photolithograpy. In addition, the alignment stability is provided by the first pretilt.

[0074]FIG. 13 is showing another embodiment of process for multi-domain liquid crystal cell.

[0075]FIG. 13a and FIG. 13b is showing the rubbing process to provide a 1-1th pretilt and 1-2th pretilt on a first domain I and a second domain II of the first substrate 1 with different pretilt angle, such as 1-1th pretilt angle is larger than 1-2th pretilt angle. The alignment layer for dividing domain is shown in FIG. 13a, an organic alignment layer 8A is covered with an inorganic alignment layer 8B on the first substrate 1. In the organic alignment layer 8A, pretilt angle is formed larger than in the inorganic alignment layer 8B. Thus, the 1-1th pretilt is defined a low 1-1th pretilt angle and a first pretilt angle direction, and the 1-2th pretilt is define a high 1-2th pretilt angle a first pretilt angle direction.

[0076]FIG. 13c-FIG. 13d are showing the process for two domained the second substrate 2 with dividing two pretilts by differing two pretilt angles. The substrate 2 coated with a second alignment layer 9 is covered with a mask 10 comprising of a transparent part for a first domain I and a semi-transparent part for a second domain II. The polarized light is irradiated in the perpendicular direction onto the second substrate so as to determined a high 2-1th pretilt angle, a second alignment direction and two second pretilt angle directions on a first domain I, and a low 2-2th pretilt angle and two second pretilt angle directions on a second domain II. To select a second pretilt angle direction for a first domain I and a second domain II, the nonpolarized light is irradiated in the oblique direction to the second substrate 2. Thereby, the 2-1th pretilt and 2-2th pretilt are formed on a first domain I and a second domain II, respectively, the 2-1th pretilt meaning a high 2-1 pretilt angle and a second pretilt angle direction, and the 2-1th pretilt meaning a low 2-2 pretilt angle and a second pretilt angle direction, as shown in FIG. 13e.

[0077] Assembling the first substrate 1 and the second substrate 2, liquid crystal materials are injected between two substrates 1,2. The molecules of liquid crystal materials are aligned in the different direction between domains as shown in FIG. 13f depending the pretilt angles.

[0078] Thereby, the viewing angle is compensated by differently aligning the liquid crystal molecules according to domains so as to get a wider viewing angle liquid crystal cell.

[0079] In this embodiment, the two-domain liquid crystal cell is possible to obtain multi-domain liquid crystal cell without photolithograpy. In addition, the alignment stability is provided by the rubbed first alignment.

[0080]FIG. 14 is showing a process for fabricating four-domain liquid crystal cell. A two-domain first substrate 1 is prepared by the reverse rubbing, as shown in FIG. 14a, FIG. 14b and FIG. 14c. The Four-domain second substrate 2 is prepared by changing the photo-irradiating direction, as shown in FIG. 14d-FIG. 14i.

[0081] Attaching two substrates 1,2, liquid crystal materials are injected between two substrates 1,2. The, the viewing angle is compensated by differently aligning the liquid crystal molecules according to each domain, as shown in FIG. 14g so as to get a wider viewing angle liquid crystal cell.

[0082] This invention can be adopted to the various mode liquid crystal cells such as a TN mode, a ECB mode, a bend mode, and a IPS mode by controlling the alignment direction.

[0083] In this invention, it is possible to provide alignment stability by rubbed first alignment layer, and to increase the yield by aligning using light instead of rubbing so as to eliminating damages caused by rubbing process.

[0084] In addition, the multi-domain liquid crystal cell can be obtained by simply process without a photolithograpy for reverse rubbing.

[0085] It is to be understood that the form of the present invention herein show and described is to be taken as a preferred example of the same and that various application such as the change the photo-irradiation order, may be resorted to without departing from the spirit of the present invention or the scope of the subjoined claims. 

What is claimed is:
 1. A method of manufacturing a liquid crystal display, comprising the steps of: providing a first alignment layer on a first substrate; rubbing said first alignment layer such that said first alignment layer has a first pretilt angle associated therewith; providing a second alignment layer on a second substrate; exposing said second alignment layer to light such that said second alignment layer has at least one second pretilt angle associated therewith; and providing a liquid crystal material between said first and second substrates.
 2. A method in accordance with claim 1, wherein said first alignment layer comprises polyimide.
 3. A method in accordance with claim 1, wherein said second alignment layer comprises polysiloxane based materials.
 4. A method in accordance with claim 1, wherein said light includes linearly polarized light.
 5. A method in accordance with claim 1, wherein said exposing step further comprises the steps of: generating unpolarized light; and transmitting said unpolarized light through a polarizer to generate said lincarly polarized light.
 6. A method in accordance with claim 5, wherein said linearly polarized light includes linearly polarized ultraviolet light.
 7. A method in accordance with claim 1, wherein said light is incident substantially perpendicular to said second alignment layer.
 8. A method in accordance with claim 1, wherein said light comprises ultraviolet light.
 9. A method in accordance with claim 1, wherein said exposing step includes a single exposure to said light.
 10. A method in accordance with claim 1, wherein a plurality of pretilt angles are associated with said second alignment layer after said exposing step, said plurality of pretilt angles being oriented in respective pretilt directions, said providing step further comprising the step of injecting said liquid crystal material between said first and second substrates so as to select ones of said plurality of pretilt angles oriented in a single direction.
 11. A method in accordance with claim 7, wherein said photo-incidation is further comprising the step of exposing additional light to select ones of said plurality of pretilt angles oriented in a single direction.
 12. A method in accordance with claim 11, wherein said additional light compries unpolarized light.
 13. A method in accordance with claim 12, wherein said unpolarized additional light is obliquely incident to the second alignment layer.
 14. A method in accordance with claim 1, wherein said exposing step is comprising the steps of; exposing said second alignment layer to a polarized light in the perpendicular direction; and exposing said second alignment layer to a nonpolarized light in the oblique direction.
 15. A method in accordance with claim 1, wherein said exposing step is comprising the steps of; exposing said second alignment layer to a nonpolarized light in the oblique direction; and exposing said second alignment layer to a polarized light in the perpendicular direction.
 16. A method in accordance with claim 1, wherein said exposing steps further comprises the steps of: exposing said second alignment layer to a first light such that a plurality of pretilt angles are associated with said second alignment layer, said plurality of pretilt angles being oriented in respective pretilt directions, exposing a first portion of said second alignment layer to a second light so as to select ones of said pretilt angles associated with said first portion oriented in a first direction; and exposing a second portion of said second alignment layer to a third light so as to select ones of said pretilt angles associated with said second portion oriented in a second direction.
 17. A method in accordance with claim 16, wherein said first light includes linearly polarized light.
 18. A method in accordance with claim 16, wherein said first light is incident substantially perpendicular to a surface of said second alignment layer.
 19. A method in accordance with claim 16, wherein said second light and/or said third light include/includes unpolarized light.
 20. A method in accordance with claim 19, wherein said second light and/or said third light are/is incident obliquely to said surface of said second alignment layer.
 21. A method in accordance with claim 1, further comprising the steps of: providing a third alignment layer on a portion of said first alignment layer; rubbing said third alignment layer such that said third alignment layer has a third pretilt angle associated therewith.
 22. A method in accordance with claim 21, wherein said third alignment layer has a pretilt angle forming characteristics differing than the first alignment layer's.
 23. A method in accordance with claim 21, wherein said third pretilt angle has a magnitude greater than said first pretilt angle.
 24. A method in accordance with claim 1, further comprising the steps of: exposing a first portion of said second alignment layer to a first dose of a first light such that a first plurality of pretilt angles having respective pretilt directions are associated with said first portion of said second alignment layer, and exposing a second portion of said second alignment layer to a second dose of said first light such that a second plurality of pretilt angles having respective pretilt directions are associated with said second portion of said second alignment layer.
 25. A method in accordance with claim 24, further comprising the steps of: exposing said first portion of said second alignment layer to a first dose of a second light to select ones of said pretilt angles associated with said first portion of said second alignment layer; and exposing said second portion of said second alignment layer to a second dose of said second light to select ones of said pretilt angles associated with said second portion of said second alignment layer.
 26. A method in accordance with claim 24, wherein said first light includes linearly polarized light.
 27. A method in accordance with claim 28, wherein said first light is incident substantially perpendicular to said surface of said second alignment layer.
 28. A method in accordance with claim 24, wherein said first plurality of pretilt angles each have a magnitude greater than a magnitude of each of said second plurality of pretilt angles.
 29. A method in accordance with claim 25, wherein said second light includes unpolarized light.
 30. A method in accordance with claim 25, wherein said second light is incident obliquely to said surface of said second alignment layer.
 31. A method in accordance with claim 24, wherein said first light is supplied to said second alignment layer through a plate having a first part aligned with said first portion of said substrate and having a first transmissivity, and a second part aligned with said second portion of said second alignment layer and having a second transmissivity.
 32. A method in accordance with claim 25, wherein said second light is supplied to said second alignment layer through a plate having a first part aligned with said first portion of said second alignment and having a first transmissivity, and a second part aligned with said second portion of said second alignment layer and having a second transmissivity.
 33. A method in accordance with claim 1, wherein said exposure step further comprises the steps of: exposing a first portion of said second alignment layer to a first light such that a first pretilt angle oriented in a first direction is associated with said first portion of said second alignment layer; exposing a second portion of said second alignment layer to a second light such that a second pretilt angle oriented in a second direction is associated with said second portion of said second alignment layer, exposing a third portion of said second alignment layer to a third light such that a third pretilt angle oriented in a third direction is associated with said third portion of said second alignment layer; and exposing a fourth portion of said second alignment layer to a fourth light such that a fourth pretilt angle oriented in a fourth direction is associated with said fourth portion of said second alignment layer.
 34. A method in accordance with claim 33, wherein at least ones of said lights includes unpolarized light, the lights including the first light, the second light, the third light, and fourth light.
 35. A method in accordance with claim 34, wherein at least ones of said lights is incident obliquely to said surface of said second alignment layer the lights including the first light, the second light, the third light, and fourth light.
 36. A method in accordance with claim 1, wherein the exposing step is comprising the steps of: exposing a first portion of said second alignment layer to a first polarized light in the first perpendicular direction; and exposing a second portion of said second alignment layer to a second polarized light in the second perpendisular direction
 37. A method in accordance with claim 36, wherein the exposing step is further comprising the steps of: exposing a first portion of said second alignment layer to a first unpolarized light in the first oblique direction; and exposing a second portion of said second alignment layer to a second unpolarized light in the second oblique direction.
 38. A method in accordance with claim 36, wherein the exposing step is further comprising the steps of: exposing a first area of a first portion of said second alignment layer to a first unpolarized light in a first oblique direction; exposing a second area of a first portion of said second alignment layer to a second unpolarized light in a second oblique directionand: exposing a first area of a second portion of said second alignment layer to a third unpolarized light in a third oblique direction: and exposing a second area of a second portion of said second alignment layer to a fourth unpolarized light in a fourth oblique direction.
 39. A method of manufacturing a liquid crystal display, comprising the steps of: coating a first substrate with a first alignment layer; rubbing said first alignment layer to impart a first alignment direction, a first pretilt angle direction and a first pretilt angle magnitude; coating a second substrate with a second alignment layer; exposing said second alignment layer to impart a second alignment direction, a plurality of second pretilt angles each having a second pretilt angle magnitude and oriented in a plurality of pretilt angle direction; and injecting liquid crystal material between said first and second substrates to select those of said plurality of pretilt angles oriented in one of said pretilt angle directions.
 40. A method of manufacturing a liquid crystal cell in accordance with claim 39, wherein said first alignment layer includes polyimide.
 41. A method of manufacturing a liquid crystal cell in accordance with claim 39, wherein said second alignment layer includes a polysiloxane based material.
 42. A method of manufacturing a liquid crystal cell in accordance with claim 39, wherein during said exposing step, said light is incident substantially perpendicular to said second alignment layer.
 43. A method of manufacturing a liquid crystal cell in accordance with claim 39, wherein said light comprises ultraviolet light.
 44. A method of manufacturing a liquid crystal cell in accordance with claim 43, wherein said ultraviolet light comprises linearly polarized ultraviolet light.
 45. A method of manufacturing a liquid crystal cell in accordance with claim 39, wherein said exposing step includes a single exposure of said second alignment layer to said light.
 46. A method of manufacturing a liquid crystal cell in accordance with claim 39, wherein said first pretilt angle direction is different from said second pretilt angle direction.
 47. A liquid crystal display device comprising: a first substrate; a rubbed layer provided on said first substrate; a second substrate; a photo-aliged layer provided on said second substrate; and liquid crystal material provided between said first and second substrates.
 48. A liquid crystal display device in accordance with claim 47, wherein said rubbed layer comprises polyimide.
 49. A liquid crystal display device in accordance with claim 47, wherein said photo-aliged layer comprises a polysiloxane based material.
 50. A liquid crystal display device in accordance with claim 47, wherein first molecules of said liquid crystal material adjacent said rubbed layer are aligned in a first direction, the first direction having a first pretilt angle and a first pretilt angle direction associated with said rubbed layer.
 51. A liquid crystal display device in accordance with claim 47, wherein second molecules of said liquid crystal material adjacent said photo-aligned layer are aligned in a second direction, the second direction having a second pretilt angle and a second pretilt angle direction associated with said photo-aliged layer.
 52. A liquid crystal display device in accordance with claim 47, wherein said first pretilt angle and/or said second pretilt angle are/is larger than 60°.
 53. A liquid crystal display device in accordance with claim 52, wherein said first pretilt angle and/or said second pretilt angle are/is 75°-87°.
 54. A liquid crystal display device in accordance with claim 47, wherein said first pretilt angle direction is substantially parrallel with said second pretilt angle direction.
 55. A liquid crystal display device in accordance with claim 47, wherein said first pretilt angle direction is different with said second pretilt angle direction.
 56. A liquid crystal display device in accordance with claim 55, wherein said first pretilt angle direction is substantially perpendicular to said second pretilt angle direction.
 57. A liquid crystal display device in accordance with claim 55, wherein said first pretilt angle direction is substantially anti-parallel to said second pretilt angle direction.
 58. A liquid crystal display device in accordance with claim 47, wherein pluralities of liquid crystal molecules are provided adjacent respective portions of said photo-aligned layer, each plurality of liquid crystal molecules having a corresponding pretilt angle and pretilt direction. 